硅渣和玻璃粉直接烧结制备多孔材料的气孔结构与力学性能

以硅渣和玻璃粉为原料,采用粉体直接烧结法制备多孔材料,研究了烧结温度(700~900℃)、烧结时间(15~120min)和升温速率(10~100℃·min^-1)对多孔材料表观密度、气孔率、物相组成、抗压强度的影响。结果表明:气孔结构均匀性随烧结温度的升高而降低;表观密度随烧结温度的升高先减小后增大,随保温时间的延长而增大,随升温速率的增大而减小,气孔率的变化趋势与表观密度的相反;多孔材料的主要物相为玻璃相和硅、SiC、SiO2、Ca2Al2SiO7等结晶相,且结晶度随烧结温度的升高而降低;抗压强度随烧结温度的升高呈先增大后减小的趋势;当烧结温度为750℃,升温速率为30℃·min^-1,烧结时间为30 min时,多孔材料的主晶相为硅和Ca2Al2SiO7,抗压强度最大(1.60MPa),表观密度为0.43g·cm^-3,气孔率为80%。     

稀土元素Ce对取向硅钢热轧钢带组织和织构的影响

对2250 mm热轧生产线生产的取向硅钢热轧钢带的合金体系进行了设计,制定了合理的加热制度和热轧轧制工艺。对添加稀土元素Ce的取向硅钢铸坯和热轧钢带进行了分析,探究了稀土元素Ce对取向硅钢低倍组织、热轧织构及成品磁性能的影响。结果表明,稀土元素Ce能够细化取向硅钢连铸坯低倍组织和热轧显微组织,提高取向硅钢成品磁性能。     

High-efficiency Silicon Solar Cells: A Review

Over the past few decades, crystalline silicon solar cells have been extensively studied due to their high efficiency, high reliability, and low cost. In addition, these types of cells lead the industry and account for more than half of the market. For the foreseeable future, Si will still be a critical material for photovoltaic devices in the solar cell industry. In this paper, we discuss key issues, cell concepts, and the status of recent high-efficiency crystalline silicon solar cells.     

向家坝二纵围堰柔性结构段基础施工技术初探

向家坝水电站二期纵向围堰上游段座落于厚达45～62 m的覆盖层上，为提高接头段深厚覆盖层地基承载力，且保证导流期不同江水位时的堰体稳定，优化调整方案为，将接头段和导水段改为柔性结构。详细介绍了柔性结构段基础处理中所涉及的施工程序、施工技术和异常情况处理等。二纵围堰经过了2009年和2010年两个汛期的考验，安全监测显示与实际运行表明，柔性结构体结构稳定。将导水结构堰体改为柔性结构体，不仅节约了投资，而且保证了二期截流工程按施工总进度计划实施。     

CO2 detection with CNx thin films deposited on porous silicon

In recent years, porous silicon (PSi) has attracted a great deal of attention for sensing applications. However, the high reactivity of PSi surfaces causes serious problems of stability. In this work, we developed new thin films that can serve as stabilizer of PSi for CO₂ gas sensors development. PSi surface was coated with carbon nitride (CN_x) film which is one of the most important interfering to stabilize the PSi layer. CN_x film was deposited by pulsed laser ablation. The effect of CO₂ gas on the sensor response was investigated for different polarization voltages. The electrical properties of (Al/CN_x/PSi/Si) structure were modified in the presence of the gas. The device shows a high sensitivity against CO₂ gas. Furthermore, the current variation of the sensor as a function of time has been investigated. The results show that the Al/CN_x/PSi/Si structure becomes stable after the first two weeks.     

Control-faced dynamics with deformation compatibility for a 5-DOF active over-constrained spatial parallel manipulator 6PUS–UPU

Taking into account the effect of structural compliance, inverse dynamics of the active over-constrained parallel manipulator 6PUS–UPU with five degrees of freedom is solved in this article. Firstly, the relationship between driving forces and actuated force screws of each limb is derived. Then the coordination of elastic deformation between limbs which consider the effect of gravity and inertia is acquired. Finally the unique solution of driving forces for the active over-constrained parallel manipulator is derived by incorporating the force equilibrium equation of the moving platform. To validate the theoretical derivation, dynamics simulation model of manipulator based on rigid–flexible mixed structure is shown and numerical examples are given. Comparison with the traditional method of dynamics based on pseudo-inverse is also made. Finally, a feasible experimental method, as an effective test to the theoretical calculation, is proposed and applied on the prototype.     

多晶硅原辅料中碳杂质的分析

碳杂质是多晶硅产品的重要杂质之一。为了更好的控制多晶硅产品中的碳杂质,需要明确碳杂质在生产中的分布及转化原理,寻找控制产品中碳杂质的途径。通过分析多晶硅生产中原辅料中碳杂质的来源和控制方式,进而控制产品中碳杂质。     

Novel SiC synthesis method applicable to SiC solid phase sintering

Most of the present production processes of SiC sintered bodies require some powder mixing using a mechanical milling process (ball milling, and so on). In this case, relatively long hours are required, and there is the problem of contamination during the preparation process. To avoid these problems, we developed a new process for obtaining a self-sinterable, stoichiometric SiC powder, whose precursor material is water-soluble; the precursor material was synthesized from aqueous silica and citric acid containing a small amount of aluminum compound. In order to obtain the stoichiometric SiC composition, the above aqueous precursor material was adequately cured in air (200°C-400°C); subsequently carbonization reaction (~800°C) in nitrogen atmosphere, carbothermal reduction (~1600°C) in argon atmosphere, and pressureless sintering (~1900°C) were performed. Among these processes, the curing process (cross-linking process) is very important for obtaining the equivalent composition (silica and carbon) for the subsequent carbothermal reduction. In this study, the adequate curing temperature and suitable preparation condition for the carbothermal reduction were investigated for the production of stoichiometric self-sinterable SiC powder. The pressureless sintered body achieved using the obtained SiC powder demonstrated a desirable trans-crystalline fracture behavior.     

X射线荧光光谱法测定氧化铝中杂质含量的质量控制方法

为满足本公司生产需求,实验室采用X射线荧光光谱法(XRF)测定氧化铝中SiO₂、Fe₂O₃、Na₂O含量,而XRF检测结果的准确性取决于日常质量控制效果。工作中总结出一套以XRF设备分析原理为基础结合氧化铝中SiO₂、Fe₂O₃、Na₂O测定经验的有效质量控制方法,论述了质量控制计划制定的依据及质量控制方法选择的原则,从仪器设备检测状态控制、样品制备方法选择、XRF漂移校正、标准样品检测、方法比对、人员比对及留样再测等方面详细介绍了内部质量控制方法,同时运用实验室间比对及测量审核两种外部质量控制方法对内部质量控制效果进行检验。通过统计分析内外部质量控制数据,发现实验室用XRF测定粉末压片法制样的氧化铝中SiO₂、Fe₂O₃、Na₂O含量,检测结果准确可靠,证明质量控制方法有效。该套质量控制经验对于XRF测定其他材料中杂质元素含量的质量控制方法的建立同样具有参考借鉴意义。